Kajian Eksperimental Sifat Mekanik Panel Cross Laminated Timber Kayu Sengon dan Kayu Jabon

Sari

ABSTRAK

Panel Cross Laminated Timber (CLT) merupakan rekayasa kayu dengan penyusunan kayu dengan arah bersilangan 90  Material kayu yang digunakan yaitu kayu Sengon dan kayu Jabon. Pembuatan panel CLT menggunakan perekat Polyvinyl Acetate, Cross-linker, dan Lateks Karet Alam dengan perbandingan 1:1 untuk base dan 15% untuk katalisator. Tujuan dari penelitian ini, untuk mengetahui kinerja panel CLT kayu Sengon dan kayu Jabon terhadap beban tekan dan geser. Pembuatan panel CLT dilakukan dengan menggunakan kempa dingin dan dimensi panel CLT yang digunakan yaitu 950mm 950mm 120mm. Hasil pengujian eksperimental pada benda uji small clear, didapatkan bahwa kayu jabon dan kayu sengon masuk kedalam kelas kuat V. Kapasitas tekan panel CLT kayu Sengon lebih kuat dibandingkan CLT Jabon yaitu 12,196 MPa dengan defleksi 10,51 mm dan kapasitas tekan panel CLT Kayu Jabon 9,572 MPa dengan defleksi 2,67. Pada pengujian kuat geser Panel CLT kayu Sengon menghasilkan nilai kuat geser lebih baik dari pada CLT kayu Jabon sebesar 0,09 MPa, dan kuat geser CLT kayu Jabon 0,089 MPa.

Kata kunci: cross laminated timber, perekat, kuat tekan, kuat geser, defleksi.

 

ABSTRACT

Cross Laminated Timber (CLT) Panel Is wood engineering with wood’s arrangement cross direction 90°. Wood materials used Sengon and Jabon. Making CLT panels using Polyvinyl Acetate, Cross-linker, and Natural Rubber Latex adhesives with a ratio of 1:1 for base and 15% for catalyst. The purpose of this research is to know the performance of Sengon and Jabon wood CLT panels against press and shear load. CLT panel is made by used cold press processed and the CLT panel dimensions used is 950mm 950mm 120mm. The results of small clear test object, found that Jabon wood and sengon wood were included in the strong V class.The compressive capacity of Sengon wood CLT panel is stronger than Jabon CLT which is 12.196 MPa with 10.51 mm deflection and the compressive capacity of Jabon CLT panel is 9.572 MPa with a deflection of 2.67. The shear strength testing of Sengon wood CLT Panel produces better shear strength than Jabon wood. Shear strength Sengon’s CLT is 0.089 MPa and Jabon’s CLT is 0.128 MPa.

Keywords: cross laminated timber, glue, compression strength, shear strength, deflection.